TY - JOUR TI - Degradation behaviour in vitro of poly L-lactic acid (PLLA)/polycaprolactone (PCL) masterbatch AU - Liu, Shu-Qiang AU - Wang, Kai-Wen AU - Yang, Ya-Ru AU - Li, Hui-Min AU - Wu, Gai-Hong AU - Yu, Juan-Juan AU - Liu, Ming-Fang AU - Zang, Yao AU - Wang, Peng AU - Zhang, Jie AU - Xu, An AU - Yin, Xiao-Long AU - Li, Fu AU - Zhang, Man T2 - Industria Textila AB - In order to prepare the absorbable medical textile material with different degradation rates, two biopolymers of poly L-lactic acid (PLLA) and polycaprolactone (PCL) with different degradation rates, were mixed in different proportions, and made into PLLA/PCL masterbatch. The experiment of degradation in vitro was conducted to reveal the degradation behaviour of PLLA/PCL masterbatch, and the characteristics of masterbatch in degradation, such as surface morphol- ogy, chemical structure, crystallization, mass loss and strength, were analyzed. The results indicated that the surface of PLLA/PCL masterbatch was etched in degradation, and the larger proportion of PCL, the less etching and slower degra- dation. The ester bonds were hydrolyzed firstly, and the crystallization region in PLLA/PCL masterbatch was destroyed gradually to form a non-crystalline region in degradation. The degradation rate of PLLA in composite masterbatch was faster than that of PCL. With increasing of PCL involved in masterbatch, the mass loss rate of masterbatch in degrada- tion decreased. In addition, the more PCL involved in composite masterbatch, the lower breaking strength. DA - 2020/04/30/ PY - 2020 DO - 10.35530/IT.071.02.1628 DP - DOI.org (Crossref) VL - 71 IS - 02 SP - 99 EP - 104 SN - 12225347 UR - http://revistaindustriatextila.ro/images/2020/2/001_SHU-QIANG%20LIU_Industria%20Textila%20no%202_2020.pdf Y2 - 2020/05/26/09:46:19 ER -